PolyWood™ features Polymakers Jam-Free™ technology and Polymakers Stabilized Foaming™ technology:

Jam-Free™ technology improves the heat stability of Polymaker’s PLA filaments with softening temperatures over 140 °C. As a result, Polymaker’s PLA filaments show minimal softening in the “cold end” and can melt rapidly once entering the heating zone, leading to excellent printing quality with zero risk of nozzle jams.

Stabilized Foaming™ technology is used to produce foamed filaments, whose foam structure can survive the printing process and be inherited by the printed parts. This enables light weight 3D printed parts with unprecedented surface finish.

Features:

Light Weight - The density of PolyWood™ is on average 0.8 g/cm³ which is 35- 40% lighter than regular PLA.

Wood with no mess - Instead of using wood to mimic wood, Polymaker developed a unique foaming technology to deliver a material that mimics wood structurally. PolyWood™ is composed entirely of polymers. The Results? Excellent print quality without the risk of nozzle jams.

Next >

Print Settings

Nozzle Temperature: 190°C – 210°C
Printing Speed: 35mm/s – 50mm/s
Bed Temperature: 25°C – 60°C
Bed Surface: Glass with glue, blue tape, BuilTak®
Cooling Fan: ON

Mechanical Properties

Young’s Modulus: N/A
Tensile Strength: 23.2 ± 0.4 Mpa
Bending Strength: 52.9 ± 0.3 Mpa
Impact Strength: 2.1 ± 0.2 kJ/m2

Thermal Properties

Glass Transition Temperature: 62°C
Vicat Softening Temperature: 60°C
Melting Temperature: 151°C

Notes

Drying Settings: 70°C for 8h
Recommended Support Materials: PolyDissolve™ S1, PolySupport™


Dimensions: 224x224x65